Certificate of Test QUOTE No.: NC8635
REPORT No.: FNC12950
COMBUSTIBILITY TEST FOR MATERIALS IN ACCORDANCE WITH AS 1530.1-1994 TRADENAME:
Haymes Rendertex Renderbase Q Range Product β PM (polymer modified) Coarse Off White
SPONSOR:
Henry Haymes Proprietary Limited trading as Haymes Paints 1 Waringa Drive BALLARAT VIC 3355 AUSTRALIA
DESCRIPTION OF TEST SAMPLE:
The sponsor described the tested specimen as a coarse grade polymer-modified cement based render comprised of graded sand, crystalline silica, Portland cement, calcium hydroxide and non-hazardous ingredients. Nominal thickness: Nominal density: Colour:
50 mm 1478.31 kg/mΒ³ (measured) off white
The test result only relates to the specimen tested and described in this report. CSIRO was not involved in the selection of the materials. TEST PROCEDURE:
Five (5) samples were tested in accordance with Australian Standard 1530 Methods for fire tests on building materials, components and structures, Part 1- 1994: Combustibility Test for Materials. An alternative suitable insulating material was used to fill the annular space between the furnace tubes, as specified in Clause 4.2 of ISO 1182:2010.
RESULTS:
The following calculated results were obtained, refer also to Summary of measurements: Arithmetic mean
DESIGNATION:
=
πΊ πππππππ π
Mean furnace thermocouple temperature rise (oC)
0.85
Mean specimen centre thermocouple temperature rise (oC)
0
Mean specimen surface thermocouple temperature rise (oC)
0.59
Mean duration of sustained flaming (s)
0
Mean mass loss (%)
7.29
The material is NOT deemed combustible according to the test criteria specified in Clause 3.4 of AS 1530.1-1994.
These test results relate only to the behaviour of the test specimens of the material under the particular conditions of the test and they are not intended to be the sole criterion for assessing the potential fire hazard of the material in use. DATE OF TEST:
2 August 2022 th
Issued on the 30 day of August 2022 without alterations or additions.
Faustin Molina Testing Officer End of Report
Stephen Smith Team Leader, Reaction to Fire & Façade Fire Laboratory
Copyright CSIRO 2022 Β©. Copying or alteration of this report without written authorisation from CSIRO is forbidden. NATA Accredited Laboratory Number: 165 Corporate Site No 3625 Accredited for compliance with ISO/IEC 17025 - Testing.
Page 1 of 2